TP70 Electroplated silver （Bonding powder）
Product Description:
Electroplated silver Bonding powder TP70 epoxy/polyester hybrid powder coating, in addition to providing high decorative and protective properties, the color is more stable, better heat resistance.
Application:
Electroplating silver can be coated with manual or automatic electrostatic spray guns. The paint can be recycled using a suitable recycling system.
Film Performance:
Chemical Type |
Epoxy/Polyester Type |
Particle size |
suitable for spraying |
Specific weight |
1.2-1.7g/cm3 |
Storage conditions |
Dry and cool place |
Effective date |
12 months (25°C) |
Curing conditions |
200°C 10 minutes (MT),180°C 15 minutes (MT) |
Test Conditions:
All chemical and physical properties are laboratory test results (except where specifically stated) under specific conditions and are for reference only for coating applications. Actual product performance still depends on the end-use environment of the product.
Substrate |
sheet iron |
Pre-process |
Zinc phosphate |
Recommended film thickness |
60-80 microns (70um test film thickness) |
Curing conditions |
200°C 10 minutes (MT),180°C 15 minutes (MT) |
Physical Properties:
Flexibility |
BS3900-E11 |
3mm Through |
Adhesion |
BS3900-E6 |
Level 0 (1mm width) |
Cupping Test |
BS3900-E4 |
7mm Pass |
Hardness |
ASTMD3363 |
≥HB |
Impact resistance |
ASTM D2794 |
≥50 cm·kg |
Chemical Properties:
Salt Spray : ASTM B117 Pass - Within 2mm (250 hours), notice that the silver powder surface will be black.
Pre-process:
All metal substrates need to be degreasing, iron-based metals are zinc or iron-based phosphor, and aluminum is recommended for chromate treatment to improve corrosion resistance.